| TYPICAL PROPERTIES (1) | | | |
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 97 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 85 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 70 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3300 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 145 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3170 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 95 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 75 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 20 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 125 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 2083 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 55 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 2670 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 209 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 187 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 191 | °C | ASTM D 648 |
| Thermal Conductivity | 0.23 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 210 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 205 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 195 | °C | ISO 75/Be |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Af |
| Metallized Haze Onset | 195 | °C | S-Plastics Method |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.26 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 24 | g/10 min | ASTM D 1238 |
| Density | 1.26 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.9 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| Melt Volume Rate, MVR at 340°C/5.0 kg | 16 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:2010/08/19 | | |